Surfactant mixtures for fabric conditioning compositions

ABSTRACT

A tumble dryer article comprising: a mixture of at least two surfactants, (i) a first surfactant present in an amount of about 5 wt. % to about 70 wt. % and having an endotherm peak temperature of from about 75° C. to about 155° C., (ii) a second surfactant present in an amount of about 30 wt. % to about 95 wt. % and having an endotherm peak temperature of from about 35° C. to about 70° C., wherein the peak temperatures of the first and second surfactant of the mixture are different from each other by at least about 1° C. as measured in a differential scanning calorimeter device and a melting transition temperature of the mixture being from about 50° C. to about 120° C.; and dispenser means for dispensing the mixture onto fabrics in a tumble dryer.

FIELD OF THE INVENTION

The present invention relates to a mixture of surfactants having at least two different endotherm peak temperatures for tumble dryer articles.

BACKGROUND OF THE INVENTION

Fabric conditioning actives applied to tumble dryer substrates generally transfer the actives onto fabrics once the actives melt inside the tumble dryer. This melting range in the dryer usually falls between 50° C. and 65° C. The melted active is then wicked from the tumble dryer substrate to the drying fabrics. It is known in the art to mix fabric conditioning actives with distributing agents to effectively transfer the actives from the substrate without staining the drying fabrics. See Rudy et al. U.S. Pat. No. 4,238,531; Marsan et al., U.S. Pat. No. 3,989,631; Edwards et al., U.S. Pat. No. 4,076,633. It is also known to mix a particular fabric conditioning active, e.g., sorbitan ester, with a fatty acid soap to modify the phase and viscosity behavior of the mixture to reduce fabric staining as described in U.S. Pat. No. 4,049,858.

These described mixtures, however, have only one melting point ranging from 38° C. to 100° C. Therefore, in melting point ranges above tumble dryer temperatures the actives do not melt effectively and are not transferred onto the fabrics.

High melting points are especially problematic in formulating desirable conditioning agents which exhibit excellent fabric care characteristics and which are environmentally friendly. See Naik et al., U.S. Pat. No. 4,137,180.

SUMMARY OF THE INVENTION

It is therefore an object of the invention to provide an article especially adapted for tumble dryers which comprises a mixture of surfactants having at least two endotherm peak temperatures which differ from each other and yet the mixture has a melting transition temperature of about 50° C. to about 120° C.

It is another object of the invention to provide a tumble dryer article which effectively transfers its fabric conditioning actives without staining the drying fabrics.

Another object of the invention is to provide an environmentally friendly mixture of surfactants which provides excellent fabric care.

The objects of the invention are achieved by combining about 5 wt. % to about 70 wt. % of a first surfactant having an endotherm peak temperature of from about 75° C. to about 155° C. and about 30 wt. % to about 95 wt. % of a second surfactant having an endotherm peak temperature from about 35° C. to about 70° C. to form a mixture. The resulting mixture has at least two endotherm peak temperatures which differ from each other by at least about 1° C. up to 40° C. and the mixture has a melting transition of temperature about 50° C. to about 120° C. The surfactant mixture is applied to a dispenser means, preferably a tumble dryer sheet.

Additional fabric conditioning actives and optional ingredients known in the art may also be added to the surfactant mixture.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

First Surfactant

The present invention relates to a mixture of surfactants applied to a tumble dryer article.

A first surfactant is present in the mixture in an amount of about 5 wt. % to about 70 wt. %, preferably 10 wt. % to about 40 wt. %, most preferably 20 wt. % to about 40 wt. %.

The first surfactant has an endotherm peak temperature of from about 75° C. to about 155° C., preferably 100° C. to about 150° C., most preferably 110° C. to about 150° C.

The endotherm peak temperature is measured by a differential scanning calorimeter device as known in the art. A particularly useful calorimeter is the DuPont 2100 device supplied by DuPont Corporation.

Suitable surfactants exhibiting this endotherm peak temperature include a water insoluble cationic fabric softening agent of formula ##STR1## wherein R₁, R₂ and R₃ are independently selected from C₁₋₄ alkyl or hydroxyalkyl groups or C₂₋₄ alkenyl groups; and wherein R₄ and R₅ are independently selected from C₇₋₂₇ alkyl or alkenyl groups; n is an integer from 0 to 5 and X represents a methyl sulfate; or a compound of formula ##STR2## wherein R is a C₇₋₂₇ alkyl or alkenyl group, preferably C₇₋₂₇ alkyl.

A preferred compound of formula I is N,N-di(tallowoyl-oxy-ethyl)-N,N-dimethyl ammonium methyl sulfate (HEMS).

A particularly useful compound of formula II is ethylene bis-stearamide supplied by Witco Company of Illinois.

The peak endotherm temperature range of the compounds of formula I is about 115° C. to 125° C.

The peak endotherm temperature range of compounds of formula II is about 110° C. to 150° C.

Second Surfactant

The second surfactant to be combined with the first surfactant described above should have a lower endotherm peak temperature in the range of about 35° C. to about 70° C. This component should comprise about 30 wt. % to about 95 wt. %, preferably 60-75%.

Compounds which are preferred as the second surfactant include long chain fatty acids having at least one stearyl functional group and nonionic compounds selected from the group consisting of a linear C₈ to C₂₂ alcohol alkoxylated with 10 to 20 moles of alkylene oxide, long chain glycerol derivatives and sorbitan derivatives. Quaternized ammonium methyl salts used as fabric conditioners are also suitable as the second surfactant.

Examples of suitable long chain fatty acid materials include stearic acid having C₁₄₋₂₂ carbons and the eutectic mixture of stearic and palmitic acid material. A commercially available eutectic mixture is 45% stearic acid and 55% palmitic acid supplied as Emersol 132 supplied by Henkel.

Examples of suitable nonionic surfactants include methyl glucoside sesquistearate, methyl glucoside dioleate, sorbitan monostearate, sorbitan monooleate, glycerol monostearate, polyethylene glycol monostearate, and C₁₄ -C₁₅ primary ethoxylated alcohol.

The mixture of the first and second surfactant must exhibit at least two peak endotherm temperatures differing from each by at least 1° C., preferably by about 10° C., most preferably by about 20° C. and up to about 40° C. difference. The mixture of the surfactants must exhibit a melting transition of from about 50° C. to about 120° C. as measured on a differential scanning calorimeter.

The endotherm peak temperature is the temperature at which maximum heat gain to the sample occurs.

Preferred combinations of the first and second surfactants include compounds of formula I with stearic acid, 45% stearic acid/55% palmitic acid, glycerol monostearate, and mixtures thereof. Another preferred embodiment includes combinations of ethylene bis-stearamide, glycerol monostearate, stearic acid, or a quaternary ammonium compound known in the art.

Without being limited by theory, it is believed that the mixture of the invention possesses a shear thinning rheology in the temperature range between the endotherm peak temperatures of the mixture of the first and second surfactant and a Newtonian rheology at temperatures greater than the endotherm peak temperature of the upper endotherm limit of the mixture. Thus, the mixture results in a stable fabric conditioning mixture which is effectively transferred in a temperature range from about 25° C. to about 80° C. without fabric staining.

Optional Fabric Conditioning Components

If additional fabric conditioning is desired, up to about 50 wt. % of a fabric conditioning agent may be included to the mixture of surfactants and selected from the following classes of compounds:

i) Cationic quaternary ammonium salts. The counterion is methyl sulfate or any halide, methyl sulfate being preferred for the drier-added articles of the invention. Examples of cationic quaternary ammonium salts include, but are not limited to:

1. Acyclic quaternary ammonium salts having at least two C₈₋₃₀, preferably C₁₂₋₂₂ alkyl chains, such as: ditallow dimethyl ammonium methylsulfate, di(hydrogenated tallow)dimethyl ammonium methylsulfate, distearyldimethyl ammonium methylsulfate, dicocodimethyl ammonium methylsulfate and the like;

2. Cyclic quaternary ammonium salts of the imidazolinium type such as di(hydrogenated tallow)dimethyl imidazolinium methylsulfate, 1-ethylene-bis(2-tallow-1-methyl)imidazolinium methylsulfate and the like;

3. Diamido quaternary ammonium salts such as: methyl-bis(hydrogenated tallowamidoethyl)-2-hydroxyethyl ammonium methyl sulfate, methyl bis(tallowamidoethyl)-2-hydroxypropyl ammonium methylsulfate and the like.

ii. Tertiary fatty amines having at least one and preferably two C₈ to C₃₀, preferably C₁₂ to C₂₂ alkyl chains. Examples include hardened tallow amine and cyclic amines such as 1-(hydrogenated tallow)amidoethyl-2-(hydrogenated tallow) imidazoline. Cyclic amines which may be employed for the compositions herein are described in U.S. Pat. No. 4,806,255 incorporated by reference herein.

iii. Carboxylic acids having 8 to 30 carbon atoms and one carboxylic group per molecule. The alkyl portion has 8 to 30, preferably 12 to 22 carbon atoms. The alkyl portion may be linear or branched, saturated or unsaturated, with linear saturated alkyl preferred. Stearic acid is a preferred fatty acid for use in the composition herein. Examples of these carboxylic acids are commercial grades of stearic acid and the like which may contain small amounts of other acids.

iv. Esters of polyhydric alcohols such as sorbitan esters or glycerol stearate. Sorbitan esters are the condensation products of sorbitol or iso-sorbitol with fatty acids such as stearic acid. Preferred sorbitan esters are monoalkyl. A common example of sorbitan ester is SPAN 60 (ICI) which is a mixture of sorbitan and isosorbide stearates.

v. Fatty alcohols, ethoxylated fatty alcohols, alkyl phenols, ethoxylated alkyl phenols, ethoxylated fatty amines, ethoxylated monoglycerides and ethoxylated diglycerides.

vi. Mineral oils, and polyols such as polyethylene glycol.

vii. Silicone oils as known in the art.

Tumble Drying Article

The fabric conditioning surfactant mixture of the invention is coated onto a dispensing means to form a tumble dryer article as known in the art. See Taylor et al., U.S. Pat. No. 5,254,269. Such dispensing means can be designed for single usage or for multiple uses.

A preferred article comprises the compositions of the invention affixed to a flexible substrate, such as a woven or non-woven cloth sheet. When such an article is placed in an automatic laundry dryer, the heat, the moisture, wicking mechanism due to distribution forces and tumbling action of the dryer removes the composition from the substrate and deposits it on the fabrics.

Suitable materials which can be used as a substrate in the invention herein include, among others, sponges, paper, and woven and non-woven cloth, all having the necessary absorbancy requirements as described in Taylor, U.S. Pat. No. 5,254,269 herein incorporated by reference.

In applying the fabric conditioning composition to an absorbant substrate, the composition amount impregnated into and/or coated onto the substrate is generally in the weight ratio range of from 10:1 to 0.5:1 based on the ratio of total conditioning composition to dry, untreated substrate (fiber+binder). Preferably, the amount of the conditioning composition ranges from about 5:1 to about 1:1, most preferably from about 3:1 to 1:1, by weight of the dry, untreated substrate.

Optional Additives

It is understood that optional ingredients may be included in the composition including, among others, perfumes, dyes, pigments, brighteners or fluorescent agents, colorants, germicides, bacteriocides and preservatives. The amount of each additive in the composition is up to about 0.5% by weight.

The following examples will more fully illustrate the embodiments of this invention. All parts, percentages and proportions referred to herein and in the claims are by weight unless otherwise indicated.

EXAMPLE 1

The following compositions were prepared by admixing varying amounts of N,N-di(tallowoyl-oxy-ethyl)-N,N-dimethyl ammonium methyl sulfate (HEMS) with fatty acids as follows:

                                      TABLE 1                                      __________________________________________________________________________                          Lower            Melting                                                       Endotherm                                                                              Upper    Transition                                           Eutectic mixture                                                                        Peak    Endotherm Peak                                                                          Temperature                                  HEMS.sup.1 (% by                                                                       of Fatty Acids.sup.2                                                                    Temperature                                                                            Temperature                                                                             of Mixture                               Sample                                                                             wt.     (% by wt.)                                                                              (°C.) of mixture                                                                (°C.) of mixture                                                                 (°C.)                             __________________________________________________________________________     1    0      100      56      --       --                                       2   10      90       56      72       83                                       3   25      75       56      76       88                                       4   40      60       55      78       89                                       5   50      50       54      81       93                                       6   70      30       53      93       101                                      __________________________________________________________________________      .sup.1 Supplied by Hoechst Celanese of Germany.                                .sup.2 A mixture of 45 wt. % stearic acid/55 wt. % palmitic acid supplied      as Emersol 132 by Emersol 132 supplied by Henkel.                        

Each mixture was prepared by heating the HEMS and fatty acid component to a temperature of 125° and cooling at room temperature for 15 minutes.

The upper and lower endotherm peak temperatures, as well as the melting transition temperature, of each sample were determined with a differential scanning calorimeter supplied as a DuPont 2100 device by DuPont Company of Delaware. The calorimeter was run at a scanning temperature rate of 10° C. per minute from -45° C. to 125° C. The peak temperatures were assigned at the point at which the heat flow into each sample was at its maximum.

EXAMPLE 2

The rheologies of samples 3, 5 and 6 of Example 1 were determined by a conventional method using a rheometer supplied as a Haake Rotovisco (RV 100), using an NV sample holder geometry. Shear sweeps of from 0 to 2000 s⁻¹ were performed at the specified temperatures.

Temperatures were maintained by means of a circulating bath which jacketed the sample holder.

The following rheology data was obtained from samples 3, 5 and 6:

                  TABLE 2                                                          ______________________________________                                              Ratio of                                                                       HEMS/Eu-                                                                       tectic Mix-                                                                              Scanning                                                        Sam- ture of   Temper-                                                         ple  Fatty Acids                                                                              ature    50 s-1  100 s-1 800 s-1                                ______________________________________                                         3    25/75     65° C.                                                                            458 mPas                                                                               252 mPas                                                                               83 mPas                                              70° C.                                                                            358 mPas                                                                               236 mPas                                                                               77 mPas                                              75° C.                                                                            133 mPas                                                                               91 mPas                                                                                32 mPas                                              80° C.                                                                            30 mPas                                                                                23 mPas                                                                                15 mPas                                              85° C.                                                                            29 mPas                                                                                19 mPas                                                                                9 mPas                                5    50/50     75° C.                                                                            879 mPas                                                                               467 mPas                                                                              107 mPas                                              80° C.                                                                            141 mPas                                                                               96 mPas                                                                                67 mPas                                              85° C.                                                                            77 mPas                                                                                61 mPas                                                                                51 mPas                               6    70/30     90° C.                                                                           1692 mPas                                                                              1141 mPas                                                                              320 mPas                                              112° C.                                                                           108 mPas                                                                               99 mPas                                                                                98 mPas                               ______________________________________                                    

It was observed that each of the 3 samples exhibited a shear thinning rheology between the peak endotherm temperatures of the mixture of the two surfactants and a Newtonian rheology at temperatures above the upper endotherm peak temperature of the mixture.

EXAMPLE 3

The following samples were prepared by admixing various amounts of HEMS with a mixture of glycerol monostearate and polyethyleneglycol monostearate:

                                      TABLE 3                                      __________________________________________________________________________                             Lower   Upper   Melting                                         Glycerol                                                                             Poly-    Endotherm                                                                              Endotherm                                                                              Transition                                      Mono- ethylene Peak    Peak Tempera-                                                                          Temperature                                     stearate                                                                             Glycol Mono-                                                                            Temperature                                                                            ture (°C.) of                                                                   of Mixture                             Sample                                                                             HEMS.sup.1                                                                          (% by wt.).sup.2                                                                     stearate.sup.3                                                                          (°C.) of Mixture                                                                Mixture (°C.)                           __________________________________________________________________________      7  10   70    20       53      --      --                                      8  25   65    10       55      69      72                                      9  30   50    20       56      74      78                                     10  30   60    10       59      73      80                                     11  40   40    20       60      82      85                                     12  45   45    10       61      82      85                                     __________________________________________________________________________      .sup.1 Supplied by Hoechst Celanese of Germany.                                .sup.2 Supplied by Unichema of England                                         .sup.3 Material having an average of 4 EOs and supplied by Sherex Co.    

The samples were prepared by heating the components to a temperature of 125° C. and cooling for 30 minutes at room temperature. Rheology data for Sample 8 were obtained as described in Example 2 as follows:

                  TABLE 4                                                          ______________________________________                                                   Temper-                                                              Sample    ature    50 s-1    100 s-1 800 s-1                                   ______________________________________                                         25 HEMS/65                                                                               70° C.                                                                           1067   mPas 507  mPas 163  mPas                             GMS/10 PEG                                                                               75° C.                                                                           70     mPas 56   mPas 48   mPas                                       80° C.                                                                           58     mPas 47   mPas 39   mPas                                       90° C.                                                                           48     mPas 37   mPas 28   mPas                                       100° C.                                                                          39     mPas 29   mPas 20   mPas                             ______________________________________                                    

It was observed that the sample containing 25 wt. % HEMS exhibited shear thinning rheology between the peak endotherm temperatures of the mixture and a Newtonian rheology at temperatures above the upper endotherm peak temperatures.

EXAMPLE 5

Lower and upper endotherm peak temperatures as well as the melting transition temperatures of samples 13-21 were obtained as described in Example 1 as follows:

                                      TABLE 5                                      __________________________________________________________________________                                       Higher                                                                 Lower   Endotherm                                                                             Melting                                                         Endotherm                                                                              Peak   Transition                                         Glycerol     Peak    Temperature                                                                           Tempera-                                  Cationic                                                                            Fatty                                                                              Mono-                                                                               Ethylene bis-                                                                          Temperature of                                                                         of Mixture                                                                            ture of                               Sample                                                                             Material.sup.1                                                                      Acid.sup.1                                                                         stearate.sup.2                                                                      stearamide.sup.3                                                                       Mixture (°C.)                                                                   (°C.)                                                                          Mixture (°C.)                  __________________________________________________________________________     13  52.500                                                                              22.500                                                                             25.000                                                                              0       58.8            65                                   14  51.975                                                                              22.275                                                                             24.750                                                                              1       61.9            67                                   15  50.925                                                                              21.825                                                                             24.250                                                                              3       58.3    85.0    90                                   16  49.875                                                                              21.375                                                                             23.750                                                                              5       61.2    92.3    98                                   17  49.350                                                                              21.150                                                                             23.500                                                                              6       59.5    92.2   103                                   18  48.825                                                                              20.925                                                                             23.250                                                                              7       59.9    93.1   103                                   19  48.300                                                                              20.700                                                                             23.000                                                                              8       59.4    93.5   102                                   20  47.775                                                                              20.475                                                                             22.750                                                                              9       60.3    97.5   104                                   21  47.250                                                                              20.250                                                                             22.500                                                                              10      61.0    98.9   105                                   __________________________________________________________________________      .sup.1 Mixture of distearyl dimethyl ammonium methyl sulfate and stearic       acid supplied by Sherex as DPSC 44435                                          .sup.2 GMS supplied by Unichema                                                .sup.3 Supplied as Kemamide (W40) by Witco.                              

It was observed that ethylene bis-stearamide material combined with both a fatty acid and nonionic exhibited endotherm peak temperatures within the desired range. A cationic material was added to the samples to provide fabric conditioning characteristics.

EXAMPLE 6

Rheology data was obtained for sample 21 as described in Example 2 as follows:

                                      TABLE 6                                      __________________________________________________________________________                                Viscosity at                                                                          Viscosity at                                     Cationic                                                                            Stearic Fatty                                                                             Ethylene bis-                                                                         20/sec (mPas                                                                          800/sec                                      Sample                                                                             Material                                                                            Acid   GMS stearamide                                                                            sec)   (mPas sec)                                   __________________________________________________________________________     21  47.25                                                                               20.25  22.50                                                                              10     604    280                                          __________________________________________________________________________

EXAMPLE 7

Tumble dryer sheet staining tests were run for several of the compositions. The test evaluated the amount of oil-like stains transferred from the dryer sheet to 100% polyester pongee cloths.

Ten pongee cloths each having 20 by 30 inch dimension were placed in a Kenmore 80 series washing machine with enough cotton bulk cloth to have a total dry load weight of three pounds. The cloths were put through a cold water rinse in a spin cycle.

A Lady Kenmore tumble dryer was preheated for 15 minutes until the dryer air temperature reached at least 115° F. Upon completion of the rinse spin cycle, the load was transferred to the preheated dryer. Dryer sheets tested were weighed and individually placed into the dryer and tumble dried with the load for thirty minutes on a cotton/sturdy cycle.

Upon completion of the dryer cycle, the dryer air temperature and sheet weight was recorded. The polyester swatches were removed from the dryer and graded for staining under northern daylight using the following rating scale:

    ______________________________________                                         RATINGS            DESCRIPTION                                                 ______________________________________                                         0                  No staining                                                 1                  Trace staining                                              2                  Slight staining                                             3                  Moderate staining                                           4                  Heavy staining                                              5                  Extreme staining                                            ______________________________________                                    

The actives on the dryer sheets which were evaluated, the original coating weight of the active, the release weight of the active and the staining score are as follows:

    ______________________________________                                                   COATING               AVERAGE                                                  WEIGHT      RELEASE   STAINING                                       SAMPLES   (GRAMS)     (GRAMS)   SCORE                                          ______________________________________                                         Control.sup.1                                                                            1.6         0.62      0.95                                                     2.0         0.90      2.65                                                     2.3         1.18      2.95                                           1.sup.2   2.6         2.3       3.2                                            3.sup.3   2.6         2.0       1.7                                            4.sup.4   2.6         1.7       0.8                                            6.sup.5   2.6         0.8       0.2                                            8.sup.6   1.6         0.93      2.6                                                      1.6         0.74      2.8                                                      2.3         0.83      2.0                                            12.sup.7  2.6         0.64      1.3                                            ______________________________________                                          .sup.1 70 wt. % distearyl dimethylammoniummethyl sulfate and 30% eutectic      mixture of fatty acids supplied as Emersol 132 and mixed as described in       Example 1.                                                                     .sup.2 100 wt. % Emersol 132.                                                  .sup.3 25 wt. % HEMS and 75 wt. % Emersol 132.                                 .sup.4 40 wt. % HEMS and 60 wt. % Emersol 132.                                 .sup.5 70 wt. % HEMS and 30 wt. % Emersol 132.                                 .sup.6 25 wt. % HEMS and 65 wt. % Glycerolmonostearate and 10 wt. %            Polyethyleneglycol monostearate.                                               .sup.7 45 wt. % HEMS and 45 wt. % Glycerolmonostearate and 10 wt. %            Polyethyleneglycol monostearate.                                         

The staining scores from sheets comprised of 70 wt.% of distearyl dimethylammonium methyl sulfate and 30 wt. % of eutectic fatty acids supplied as Emersol 132, are also shown as controls. The staining score of this active mixture increases dramatically with an increase of its coating weight. Sample #1, which comprised of Emersol 132 only, stained the treated fabric heavily.

Samples #3, #4 and #6, which contained mixtures of HEMS and Emersol 132 of various proportions, showed significant reduction of staining compared with the control and released more active to treated fabrics. These samples clearly demonstrated the effective transfers of their actives without staining the drying fabrics severely.

Sample #8 and #12, which are comprised of mixture of HEMS, glycerol monostearate and polyethylene glycol monostearate, also exhibited lower staining scores compare with the control of similar coating weights.

EXAMPLE 8

Two formulations were prepared by admixing HEMS with stearic acid and polyethyleneglycol monostearate in various proportions and as described in Example 1. The two formulations were coated onto a dryer sheet and tested for staining as described in Example 6 with the following results:

                  TABLE 8                                                          ______________________________________                                                       COATING             AVERAGE                                                    WEIGHT    RELEASE   STAINING                                     FORMULATION   (GRAMS)   (GRAMS)   SCORE                                        ______________________________________                                         45 HEMS/45 Stearic                                                                           1.6       0.53      1.0                                          Acid/10                                                                        Polyethylene glycol                                                            Monostearate                                                                   16 wt. % HEMS/64                                                                             1.6       0.94      2.0                                          wt. % stearic acid/                                                            20 wt. %                                                                       Polyethylene glycol                                                            Monostearate                                                                   ______________________________________                                    

HEMS having a high endotherm peak temperature exhibited only slight to trace staining when combined with both a fatty acid and a nonionic.

EXAMPLE 9

The following formulations were tested for staining as described in Example 6.

    ______________________________________                                                   COATING               AVERAGE                                                  WEIGHT      RELEASE   STAINING                                       SAMPLE    (GRAMS)     (GRAMS)   SCORE                                          ______________________________________                                         Control.sup.8                                                                            1.6         0.67      2.0                                                      2.3         1.1       2.9                                            21.sup.9  1.6         0.52      1.4                                                      2.3         0.74      2.0                                            ______________________________________                                          .sup.8 DPSC 44435 supplied by Sherex is 52.5 wt. %                             distearyldimethylammoniummethylsulfate and 22.5 wt. % stearic acid. The        DPSC was mixed with 25 wt. % glycerolmonostearate.                             .sup.9 47.25 wt. % distearyldimethylammoniummethylsulfate and 20.25 wt. %      stearic acid supplied by Sherex, 22.6 wt. % glycerol monostearate and 10       wt. % ethylene bisstearamide.                                            

It was observed that the addition of the ethylene bis-stearamide component having an upper endotherm peak temperature of 148° reduced staining over the formulation containing only the distearyl dimethyl ammonium methyl sulfate stearic acid and GMS components. 

What is claimed is:
 1. A tumble dryer article comprising:(a) a mixture of at least two surfactants,(i) a first surfactant present in an amount of about 5 wt.% to about 70 wt.% and having an endotherm peak temperature of from about 75° C. to about 155° C., the first surfactant selected from the group consisting of N,N-di(tallowoyl-oxy-ethyl)-N,N-dimethyl ammonium methyl sulfate, N,N-di(tallowoyl-oxy-propyl)-N.N-dimethylammonium methyl sulfate, ethylene bis-stearamide and mixtures thereof, (ii) a second surfactant present in an amount of about 30 wt.% to about 95 wt.% and having an endotherm peak temperature of from about 35° C. to about 70° C., the second surfactant selected from the group consisting of long chain fatty acids, a glycerol derivative, a C₈ -C₂₀ alkoxylated alcohol and mixtures thereof, wherein the mixture has at least two endotherm peak temperatures different from each other by at least about 1° C. up to about 40° C. as measured in a differential scanning calorimeter device and a melting transition temperature about 50° C. to about 120° C.; and (b) dispenser means for dispensing the mixture onto fabrics in a tumble dryer.
 2. A tumble dryer article according to claim 1 wherein the mixture exhibits a shear thinning rheology in a temperature range between the endotherm peak temperatures of the first and second surfactants and exhibits a Newtonion rheology at a temperature above the melting temperature of the mixture.
 3. A tumble dryer article according to claim 1 wherein the first surfactant is N,N-di(tallowoyl-oxy-ethyl)-N,N-dimethyl ammonium methyl sulfate.
 4. A tumble dryer article according to claim 1 wherein the long chain fatty acid is selected from the group consisting of a stearic acid, a eutectic mixture of 45 wt. % stearic acid and 55 wt. % palmitic acid, and mixtures thereof.
 5. A tumble dryer article according to claim 1 wherein the glycerol derivative is selected from the group consisting of methyl glucoside sesquistearate, methyl glucoside dioleate, sorbitan monostearate, sorbitan monooleate, glycerol monostearate, polyethylene glycol monostearate, and mixtures thereof.
 6. A tumble dryer article according to claim 1 wherein the alkoxylated alcohol is a C₁₄ -C₁₅ primary ethoxylated alcohol.
 7. A tumble dryer article according to claim 1 wherein the mixture comprises from about 10 wt. % to about 40 wt. % of N,N-di(tallowoyl-oxy-ethyl)-N,N-dimethyl ammonium methyl sulfate and about 40 wt. % to about 90 wt. % of a long chain fatty acid.
 8. A tumble dryer article according to claim 7 wherein the fatty acid of the mixture is a stearic acid or eutectic mixture of stearic acid and palmitic acid.
 9. A tumble dryer article according to claim 1 wherein the mixture comprises from about 10 wt. % to about 40 wt. % of N,N-di(tallowoyl-oxy-ethyl)-N,N-dimethyl ammonium methyl sulfate and about 40 wt. % to about 90 wt. % of a glycerol derivative.
 10. A tumble dryer article according to claim 9 wherein the glycerol derivative is glycerolmonostearate, polyethylene glycol monostearate and mixture thereof.
 11. A tumble dryer article according to claim 1 wherein the first surfactant is ethylene bis-stearamide and the second surfactant is selected from the group of a long chain fatty acid, a glycerol derivative and mixtures thereof.
 12. A tumble dryer article according to claim 1 further comprising a fabric softener component selected from the group consisting of a cationic quaternary ammonium salt, a tertiary fatty amine having at least one C₈ to C₃₀ alkyl chain, a carboxylic acid having 8 to 30 carbon atoms and one carboxylic group per molecule, an ester of a polyhydric alcohol, a fatty alcohol, an ethoxylated fatty alcohol, an alkyl phenol, an ethoxylated alkyl phenol, an ethoxylated fatty amine, an ethoxylated monoglyceride, an ethoxylated diglyceride, mineral oil, silicone oil and mixtures thereof.
 13. A method for conditioning fabrics comprising: contacting a fabric with a tumble dryer article in a tumble dryer, the tumble dryer article comprising:a mixture of at least two surfactants,(i) a first surfactant present in an amount of about 5 wt. % to about 70 wt. % and having an endotherm peak temperature of from about 75° C. to about 155° C., the first surfactant selected from the group consisting of N,N-di(tallowoyl-oxy-ethyl)-N,N-dimethyl ammonium methyl sulfate, N,N-di(tallowoyl-oxy-propyl)-N,N-dimethylammonium methyl sulfate, ethylene bis-stearamide and mixtures thereof, (ii) a second surfactant present in an amount of about 30 wt. % to about 95 wt. % and having an endotherm peak temperature of from about 35° C. to about 70° C., the second surfactant selected from the group consisting of long chain fatty acids, a glycerol derivative, a C₈ -C₂₀ alkoxylated alcohol and mixtures thereof, wherein the peak temperatures of the first and second surfactant of the mixture are different from each other by at least about 1° C. up to about 40° C. as measured in a differential scanning calorimeter device and a melting transition temperature of the mixture being from about 50° C. to about 120° C.; and dispenser means for dispensing the mixture onto fabrics in a tumble dryer; for conditioning fabrics in a tumble dryer. 